Descriptions Hato Acrylic Emulsion Gold Paint AG-919 is based on a 100% pure acrylic latex and combined with the best available special gold pigment to give superb bright shine of gold and excellent outdoor durability for the tropical climate. It also imparts scratch resistance and excellent adhesion. It is able to resist saponification on the alkaline substrate and to withstand the U.V. degradation from the sunlight. These explain why they are durable more than 10 years. |
| |
|
|
Uses It is suitable for substitution of gold foil covering such as temple mural, hall, door, the Buddha, shrine, etc. |
| |
|
|
|
| |
| Physical properties |
Type
|
Pure Acrylic Resin |
Colour
|
Superb brilliant golden color |
Specific gravity
|
1.08 – 1.14 |
Spreading rate
|
35 – 40 sq.m. / U.S. gallon / Coat |
Dry film thickness
|
30 – 35 microns |
Drying time
|
15 - 30 minutes |
Recoat
|
2 – 3 hours |
Application
|
Brush |
| Dilution |
Acrylic clear emulsion TG-09 |
|
| |
| Surface Preparation |
Surfaces must be thorough clean, free from oil, grease or waxy contaminant. Glossy surfaces must be dulled off with wire brush or sandpaper; this insures proper adhesion. |
|
| |
| Coating system |
| Surfaces |
Primer |
Top coat |
| Concrete, Wood, Gypsum |
AG-33 1 - 2 coats
(Diluted with clean water 10-15%) |
AG-919 1 – 2 coats
(Should be diluted with TG-09) |
|
| |
| Precaution |
Keep away from children. Avoid contact with eyes. |
|
| |
 Download Technical Data Sheet 68 kb. |